50 indium ← tin → antimony Ge ↑ Sn ↓ Pb Periodic Table - Extended Periodic Table
General
Name, Symbol, Number	tin, Sn, 50
Chemical series	poor metals
Group, Period, Block	14, 5, p
Appearance	silvery lustrous gray
Standard atomic weight	118.710(7) gmol−1
Electron configuration	[Kr] 4d10 5s2 5p2
Electrons per shell	2, 8, 18, 18, 4
Physical properties
Phase	solid
Density (near r.t.)	(white) 7.265 gcm−3
Density (near r.t.)	(gray) 5.769 gcm−3
Liquid density at m.p.	6.99 gcm−3
Melting point	505.08 K (231.93 °C, 449.47 °F)
Boiling point	2875 K (2602 °C, 4716 °F)
Heat of fusion	(white) 7.03 kJmol−1
Heat of vaporization	(white) 296.1 kJmol−1
Heat capacity	(25 C) (white) 27.112 Jmol−1K−1
Vapor pressure P(Pa) 1 10 100 1 k 10 k 100 k at T(K) 1497 1657 1855 2107 2438 2893
Atomic properties
Crystal structure	tetragonal
Oxidation states	4, 2 (amphoteric oxide)
Electronegativity	1.96 (scale Pauling)
Ionization energies (more)	1st: 708.6 kJmol−1
	2nd: 1411.8 kJmol−1
	3rd: 2943.0 kJmol−1
Atomic radius	145 pm
Atomic radius (calc.)	145 pm
Covalent radius	141 pm
Van der Waals radius	217 pm
Miscellaneous
Magnetic ordering	no data
Electrical resistivity	(0 C) 115 nΩ·m
Thermal conductivity	(300 K) 66.8 Wm−1K−1
Thermal expansion	(25 C) 22.0 µmm−1K−1
Speed of sound (thin rod)	(r.t.) (rolled) 2730 ms−1
Young's modulus	50 GPa
Shear modulus	18 GPa
Bulk modulus	58 GPa
Poisson ratio	0.36
Mohs hardness	1.5
Brinell hardness	51 MPa
CAS registry number	7440-31-5
Selected isotopes
Main article: Isotopes of tin iso NA half-life DM DE (MeV) DP 112Sn 0.97% Sn is stable with 62 neutrons 114Sn 0.66% Sn is stable with 64 neutrons 115Sn 0.34% Sn is stable with 65 neutrons 116Sn 14.54% Sn is stable with 66 neutrons 117Sn 7.68% Sn is stable with 67 neutrons 118Sn 24.22% Sn is stable with 68 neutrons 119Sn 8.59% Sn is stable with 69 neutrons 120Sn 32.58% Sn is stable with 70 neutrons 122Sn 4.63% Sn is stable with 72 neutrons 124Sn 5.79% Sn is stable with 74 neutrons 126Sn syn ~1 E5 y Beta- 0.380 126Sb
References

Tin is a chemical element in the periodic table that has the symbol Sn (Latin: stannum) and atomic number 50. This silvery, malleable poor metal that is not easily oxidized in air and resists corrosion is found in many alloys and is used to coat other metals to prevent corrosion. Tin is obtained chiefly from the mineral cassiterite, where it occurs as an oxide. It can be alloyed with copper to make bronze.

Notable characteristics

Tin is a malleable, ductile, highly crystalline, silvery-white metal; when a bar of tin is bent, a strange crackling sound known as the "tin cry" can be heard due to the breaking of the crystals. This metal resists corrosion from distilled, sea and soft tap water, but can be attacked by strong acids, alkalis, and by acid salts. Tin acts as a catalyst when oxygen is in solution and helps accelerate chemical attack. Tin forms the dioxide SnO₂ when it is heated in the presence of air. SnO₂, in turn, is feebly acidic and forms stannate (SnO₃^-2) salts with basic oxides. Tin can be highly polished and is used as a protective coat for other metals in order to prevent corrosion or other chemical action. This metal combines directly with chlorine and oxygen and displaces hydrogen from dilute acids. Tin is malleable at ordinary temperatures but is brittle when it is heated.

Allotropes

Tin's chemical properties fall between those of metals and non-metals, just as the semiconductors silicon and germanium do. Tin has two allotropes at normal pressure and temperature: gray tin and white tin.

Below 13.2 °C, it exists as gray or alpha tin, which has a cubic crystal structure similar to silicon and germanium. Gray tin has no metallic properties at all, is a dull-gray powdery material, and has few uses, other than a few specialized semiconductor applications.

When warmed above 13.2 °C tin changes into white or beta tin, which is metallic and has a tetragonal structure. Converting gray tin powder into white tin produces white tin powder. To convert powdery gray tin into solid white tin the temperature must be raised above the melting point of tin.

Gray tin can cause undesirable effects in applications where the metallic properties of tin are important, since metallic white tin will slowly convert to gray tin if it is held for a long time below 13.2 °Celsius. The metallic surface of white tin becomes covered with a gray powder which is easily rubbed off. The gray patches slowly expand until all of the tin in the object is converted from the metal to the powder, at which point it loses its structural integrity and may fall to pieces. This process is known as tin disease or tin pest. Tin pest was a particular problem in northern Europe in the 18th century as organ pipes made of tin would sometimes completely disintegrate during long cold winters. Some sources also say that during Napoleon's Russian campaign of 1812, the temperatures became so cold that the tin buttons on the soldiers' uniforms disintegrated, contributing to the defeat of the Grande Armée. However, the veracity of this story is debatable, because Napoleon would likely have foreseen this problem, and the transformation to gray tin often takes a reasonably long time.^[1] This transformation, however, may be prevented by the addition of antimony or bismuth.

Applications

Tin bonds readily to iron, and has been used for coating lead or zinc and steel to prevent corrosion. Tin-plated steel containers are widely used for food preservation, and this forms a large part of the market for metallic tin. Speakers of British English call them "tins"; Americans call them "cans" or "tin cans". One thus-derived use of the slang term "tinnie" or "tinny" means "can of beer". The tin whistle is so called because it was first mass-produced in tin-plated steel.

Other uses:

• Some important tin alloys are bronze, bell metal, Babbitt metal, die casting alloy, pewter, phosphor bronze, soft solder, and White metal.
• The most important salt formed is stannous chloride, which has found use as a reducing agent and as a mordant in the calico printing process. Electrically conductive coatings are produced when tin salts are sprayed onto glass. These coatings have been used in panel lighting and in the production of frost-free windshields.
• Most metal pipes in a pipe organ are made of varying amounts of a tin/lead alloy, with 50%/50% being the most common. The amount of tin in the pipe defines the pipe's tone, since tin is the most tonally resonant of all metals. When a tin/lead alloy cools, the lead cools slightly faster and makes a mottled or spotted effect. This metal alloy is referred to as spotted metal.
• Window glass is most often made via floating molten glass on top of molten tin (creating float glass) in order to make a flat surface (this is called the "Pilkington process").
• Tin is also used in solders for joining pipes or electric circuits, in bearing alloys, in glass-making, and in a wide range of tin chemical applications. Although of higher melting point than a lead-tin alloy, the use of pure tin or tin alloyed with other metals in these applications is rapidly supplanting the use of the previously common lead–containing alloys in order to eliminate the problems of toxicity caused by lead.
• Tin foil was once a common wrapping material for foods and drugs; replaced in the early 20th century by the use of aluminium foil, which is now commonly referred to as tin foil. Hence one use of the slang term "tinnie" or "tinny" for a small retail package of a drug such as cannabis or for a can of beer.

Tin becomes a superconductor below 3.72 K. In fact, tin was one of the first superconductors to be studied; the Meissner effect, one of the characteristic features of superconductors, was first discovered in superconducting tin crystals. The niobium-tin compound Nb₃Sn is commercially used as wires for superconducting magnets, due to the material's high critical temperature (18 K) and critical magnetic field (25 T). A superconducting magnet weighing only a couple of kilograms is capable of producing magnetic fields comparable to a conventional electromagnet weighing tons.

History

Tin (Old English: tin, Old Latin: plumbum candidum ("white lead"), Old German: tsin, Late Latin: stannum) is one of the earliest metals known and was used as a component of bronze from antiquity. Because of its hardening effect on copper, tin was used in bronze implements as early as 3,500 BC. Tin mining is believed to have started in Cornwall and Devon (esp. Dartmoor) in Classical times, and a thriving tin trade developed with the civilizations of the Mediterranean^[2][3]. However the lone metal was not used until about 600 BC. The last Cornish Tin Mine, at South Crofty near Camborne closed in 1998 bringing 4,000 years of mining in Cornwall to an end.

The word "tin" has cognates in many Germanic and Celtic languages. The American Heritage Dictionary speculates that the word was borrowed from a pre-Indo-European language. The later name "stannum" and its Romance derivatures come from the lead-silver alloy of the same name for the finding of the latter in ores; the former "stagnum" was the word for a stale pool or puddle.

In modern times, the word "tin" is often improperly used as a generic phrase for any silvery metal that comes in sheets. Most everyday materials that are commonly called "tin", such as aluminum foil, beverage cans, corrugated building sheathing and tin cans, are actually made of steel or aluminum, although tin cans (tinned cans) do contain a thin coating of tin to inhibit rust. Likewise, so-called "tin toys" are usually made of steel, and may or may not have a coating of tin to inhibit rust.

Occurrence

In 2005, China was the largest producer of tin, with at least one-third of the world's share, closely followed by Indonesia and South America, reports the British Geological Survey.

Tin is produced by reducing the ore with coal in a reverberatory furnace. This metal is a relatively scarce element with an abundance in the Earth's crust of about 2 ppm, compared with 94 ppm for zinc, 63 ppm for copper, and 12 ppm for lead. Most of the world's tin is produced from placer deposits. The only mineral of commercial importance as a source of tin is cassiterite (SnO₂), although small quantities of tin are recovered from complex sulfides such as stannite, cylindrite, franckeite, canfieldite, and teallite. Secondary, or scrap, tin is also an important source of the metal.

Tasmania hosts some deposits of historical importance, most notably Mount Bischoff and Renison Bell.

see also

Isotopes

Main article: isotopes of tin

Tin is the element with the greatest number of stable isotopes (ten), which is probably related to the fact that 50 is a "magic number" of protons. 28 additional unstable isotopes are known, including the "doubly magic" tin-100 (¹⁰⁰Sn) (discovered in 1994)^[4].

Compounds

For discussion of Stannate compounds (SnO₃^2-) see Stannate. For Stannite (SnO₂^-) see Stannite. See also Stannous hydroxide (Sn(OH)₂), Stannic acid (Stannic Hydroxide - Sn(OH)₄), Tin dioxide (Stannic Oxide - SnO₂), Tin(II) oxide (Stannous Oxide - SnO), Tin(II) chloride (SnCl₂), Tin(IV) chloride (SnCl₄)

see also

Biologic effects

Elemental tin is an essential nutrient, needed in very small amounts. The small amount of tin that is found in canned foods is not harmful to humans.

Certain organic tin compounds, organotin, such as triorganotins (see tributyltin oxide) are toxic and are used as industrial fungicides and bactericides.

See also

• International Tin Council
• Tinning
• Cassiterides
• Tin pest
• Whisker (metallurgy) (tin whiskers)

References

• Los Alamos National Laboratory: Tin

External links

• WebElements.com – Tin
• Theodore Gray's Wooden Periodic Table Table: Tin samples and castings